Description
18g Aluminum (1.0mm Wire Diameter) | ||||
Inside Diameter | Aspect Ratio | Rings Per Ounce | ||
3mm | 3.16 | 1144 | ||
1/8" | 3.28 | 1144 | ||
3.5mm | 9/64" | 3.66 | 1054 | |
3.75mm | 945 | |||
4mm | 5/32" | 4.16 | 888 | |
4.25mm |
842 | |||
11/64" | 842 | |||
4.5mm | 4.61 | 794 | ||
4.75mm | 3/16" | 758 | ||
5mm | 5.17 | 732 | ||
5.5mm | 7/32" | 5.81 | 668 | |
6mm | 15/64" | 6.33 | 621 | |
1/4" | 608 | |||
6.5mm | 568 | |||
7mm | 7.57 | 535 | ||
9/32" | 535 | |||
8mm | 5/16" | 472 | ||
10mm | 374 |
Our Anodized Aluminum mixes are designed to give you a variety of color to work with or to create a unique piece of "jump ring stew”. Occasionally we will throw a few limited quantity colors into a mix to enhance the mix. They are a surprise treat and not to be expected every time or to be found with our regular rings. If you need a set amount of each color we suggest you purchase the individual colors instead of a mix.
All of our jump rings follow the American Wire Gauge (AWG), also known as Brown and Sharpe (B&S). All sizes listed are inside diameter (I.D.), which corresponds to the size of the mandrel onto which the wire is wound. Use these I.D.'s as a guide not an absolute as springback can occur. We anodize the jump rings before they are cut so the ends are raw aluminum however with the coating thickness we use and with the thin blades we cut our jump rings with, if you close the rings properly the seam can not be seen.
Our Anodized Aluminum is anodized in house at our sister company, Premier Anodizing & Metal Finishing. The anodizing process we use is FDA approved for cookware. Premier Anodizing uses only organic dyes and is rated non-hazardous. This assures that we will never be out of stock of a color and that we have control over our quality. However, the colors can change slightly from batch to batch. We use a spectrometer to get the closest color matches possible but there still can be some differences, this is normal in the anodizing process. Therefore, you should order enough to complete your entire project. The coating is fairly hard but it can be scratched with steel.